The characteristics of NiO/β-(Al0.21Ga0.79)2O3/Ga2O3 heterojunction lateral geometry rectifiers with the epitaxial layers grown by metal organic chemical vapor deposition were measured over a temperature range from 25 °C–225 °C. The forward current increased with temperature, while the on-state resistance decreased from 360 Ω.cm²at 25 °C to 30 Ω.cm²at 225 °C. The forward turn-on voltage was reduced from 4 V at 25 °C to 1.9 V at 225 °C. The reverse breakdown voltage at room temperature was ∼4.2 kV, with a temperature coefficient of −16.5 V K⁻¹. This negative temperature coefficient precludes avalanche being the breakdown mechanism and indicates that defects still dominate the reverse conduction characteristics. The corresponding power figures-of-merit were 0.27–0.49 MW.cm⁻². The maximum on/off ratios improved with temperature from 2105 at 25 °C to 3 × 107 at 225 °C when switching from 5 V forward to 0 V. The high temperature performance of the NiO/β-(Al0.21Ga0.79)2O3/Ga2O3 lateral rectifiers is promising if the current rate of optimization continues.

 

NiO/β-(Al x Ga 1− x ) 2 O 3 /Ga 2 O 3 heterojunction lateral geometry rectifiers with diameter 50–100  μm exhibited maximum reverse breakdown voltages >7 kV, showing the advantage of increasing the bandgap using the β-(Al x Ga 1− x ) 2 O 3 alloy. This Si-doped alloy layer was grown by metal organic chemical vapor deposition with an Al composition of ∼21%. On-state resistances were in the range of 50–2180 Ω cm 2 , leading to power figures-of-merit up to 0.72 MW cm −2 . The forward turn-on voltage was in the range of 2.3–2.5 V, with maximum on/off ratios >700 when switching from 5 V forward to reverse biases up to −100 V. Transmission line measurements showed the specific contact resistance was 0.12 Ω cm 2 . The breakdown voltage is among the highest reported for any lateral geometry Ga 2 O 3 -based rectifier.